Surface processes at a polymetallic (Mn-Fe-Pb) sulfide subject to cyanide leaching under sonication conditions and with an alkaline pretreatment: Understanding differences in silver extraction with X-ray photoelectron spectroscopy (XPS)
Surface processes at a polymetallic (Mn-Fe-Pb) sulfide subject to cyanide leaching under sonication conditions and with an alkaline pretreatment: Understanding differences in silver extraction with X-ray photoelectron spectroscopy (XPS)
No hay miniatura disponible
Fecha
2021
Autores
Larrabure, G.
Chero-Osorio S.
Silva-Quiñones D.
Benndorf C.
Williams M.
Gao F.
Gamarra C.
Alarcón A.
Segura C.
Teplyakov A.
Título de la revista
Revista ISSN
Título del volumen
Editor
Elsevier B.V.
Proyectos de investigación
Unidades organizativas
Número de la revista
Abstracto
Leaching of polymetallic sulfides is often challenging due to the complexity of these systems. The main issues are related to the formation of surface by-products or to the presence of different metals that require a greater consumption of chemicals compared to that needed to extract the target metal during leaching. This latter case is followed in the present work using X-ray photoelectron spectroscopy (XPS) during the leaching of a silver-containing polymetallic (Mn-Fe-Pb) sulfide under three different cyanidation procedures: (1) conventional leaching, (2) ultrasound-assisted leaching, and (3) leaching of a sample pretreated in alkaline media. In all cases, leaching results in the build-up of Pb compounds (oxides/hydroxides) on the surface of the minerals, suggesting a mechanism in which Pb is first leached by hydroxide and cyanide and later is re-adsorbed as an external layer on the minerals. On the other hand, the effect of each process on Mn was quite distinct: 1) Conventional leaching leads to the oxidation of the sulfide (pyrite) surface and a slight increase of surface Mn species; 2) Ultrasound-assisted leaching decreases surface Mn by dissolving oxidized species, which exposes fresh sulfide surfaces and increases Ag extraction; and 3) An alkaline pretreatment at high temperature exposed fresh sulfide surfaces and decreased the surface concentration of Mn. The fact that ultrasound-assisted leaching and leaching after an alkaline pretreatment allow for a higher Ag extraction (60% and 75% of total Ag, respectively, as opposed to the 25% extracted via conventional leaching), indicates that leaching is more efficient if the surface is not oxidized and if Mn is removed from the samples, either before or during leaching. © 2020 Elsevier B.V.
Descripción
Palabras clave
XPS,
Cyanide,
Leaching,
Polymetallic,
Pretreatment,
Sonication,
Sulfide,
Surface analysis,
Ultrasound-assisted