YBa2Cu3O7 films grown onto SrTiO3 and YSZ substrates by chemical solution deposition of trifluoroacetates
YBa2Cu3O7 films grown onto SrTiO3 and YSZ substrates by chemical solution deposition of trifluoroacetates
No hay miniatura disponible
Fecha
2021
Autores
Domínguez A.B.
De Los Santos Valladares L.
Cornejo H.S.
Osorio-Anaya A.M.
Santibañez J.F.
Sovero L.S.
Barnes C.H.W.
Título de la revista
Revista ISSN
Título del volumen
Editor
Springer
Proyectos de investigación
Unidades organizativas
Número de la revista
Abstracto
We report the preparation and characterization of YBa2Cu3O7 (YBCO) films grown onto SrTiO3 and YSZ substrates by the trifluoroacetates chemical solution deposition method and following sintering with oxygen atmosphere at 860 °C. The X-ray diffraction (XRD) reveals (00?) – oriented crystallites indicating epitaxial growth of the films in the c-direction. Despite granular morphology and the presence of Y2BaCuO5 and CuO as minor secondary phases, the technique shows the successful formation of the superconducting YBCO and preventing the formation of the unwanted BaCO3 phase. Rocking curve measurements of the (005) reflection for the YBCO/SrTiO3 was fitted with one Gaussian function with full width at the half maximum (FWHM) of 0.44° confirming that it consists of YBCO crystallites with different texture. For the sample grown on YSZ, the rocking curve was fitted with two Gaussian functions, one corresponding to the YBCO layer (FWHM = 0.4°) and another to the substrate (FWHM = 0.3°). The magnetic measurements taken in zero field cooling and field cooling modes confirm the formation of the superconducting YBCO with critical temperatures (TC) 91.8 and 85.7 K for the samples grown onto YSZ and SrTiO3, respectively. The critical current density (JC) curves indirectly calculated by using the Bean´s model from the M(T) loops were JC ~ 109 A/cm2 for the sample deposited onto YSZ and JC ~ 107A/cm2 for the YBCO deposited onto SrTiO3. Overall, the difference in TC and JC values between both samples could be related to their difference in oxygen content, porosity, hole concentration per Cu ion and the presence of secondary phases. © 2021, The Author(s).
Descripción
This work was supported by the Proyectos Integrales Program from the CONCYTEC agency, project title “Fabricacion de placas superconductoras de YBaCuO” (Contract No. 018 -2020 – FONDECYT – BM). A Bustamante Domínguez and A. Osorio Anaya thank the Vice-Rector Office for Research and Postgraduate from the Universidad Nacional Mayor de San Marcos for supporting their projects B151301031 and B171301856 . 2 3 7
Palabras clave
YBCO,
Chemical solution deposition,
Superconductors,
Trifluoroacetates