Vacancy ordered γ-Fe 2 O 3 nanoparticles functionalized with nanohydroxyapatite: XRD, FTIR, TEM, XPS and Mössbauer studies
Vacancy ordered γ-Fe 2 O 3 nanoparticles functionalized with nanohydroxyapatite: XRD, FTIR, TEM, XPS and Mössbauer studies
No hay miniatura disponible
Fecha
2016
Autores
Ramos Guivar J.A.
Sanches E.A.
Bruns F.
Sadrollahi E.
Morales M.A.
López E.O.
Litterst F.J.
Título de la revista
Revista ISSN
Título del volumen
Editor
Elsevier
Proyectos de investigación
Unidades organizativas
Número de la revista
Abstracto
Vacancy ordered maghemite (γ-Fe2O3) nanoparticles functionalized with nanohydroxyapatite (HAp – Ca10(PO4) 6(OH)2) have been successfully synthesized using an inexpensive co-precipitation chemical route. Evidence for the presence of vacancy order in maghemite was shown by the superstructure lines observed in X-ray diffraction. The adsorption of carboxyl groups of citric acid (C6H8O7) onto γ-Fe2O3 nanoparticles was investigated by FTIR, XPS and Mössbauer spectroscopy. From XPS surface analysis, two binding energies related to oxygen were attributed to bindings between C6H8O7/γ- Fe2O3 and C6H8O7/HAp from an interfacial reaction promoted by strongly adsorbed H2O molecules at the surface of these nanomaterials.
Descripción
Palabras clave
X ray photoelectron spectroscopy,
Binding energy,
Hematite,
Nanoparticles,
Saturation magnetization,
Surface analysis,
Synthesis (chemical),
Temperature distribution,
X ray diffraction